Could this be caused by a trim die? I could not get the bullets to seat and i have used this brass+dies before.It's .243 by the way.
Explain this if you can
- Thread starter crowsniper1
- Start date
Re: Explain this if you can
Ahah! I'm not the only one.
For me it was a case of too much annealing and excessive neck tension.
Were you neck sizing and used the wrong bushing?
I now use a mandrel expander on all cases before seating bullets. Makes for more even neck tension and fewer of these.
Ahah! I'm not the only one.
For me it was a case of too much annealing and excessive neck tension.
Were you neck sizing and used the wrong bushing?
I now use a mandrel expander on all cases before seating bullets. Makes for more even neck tension and fewer of these.
Re: Explain this if you can
Haha wow!
That must be a wildcat. Never see a shoulder like that before! Jk lol.
Haha wow!
That must be a wildcat. Never see a shoulder like that before! Jk lol.
Re: Explain this if you can
....umm....so are you considering a different chamber for your new wildcat???
....umm....so are you considering a different chamber for your new wildcat???
Re: Explain this if you can
Mntcrk is possibly on the right track or your case length/neck is too long causing a crimp action early on the bullet. I don't aneal so I can't testify to that.
Mntcrk is possibly on the right track or your case length/neck is too long causing a crimp action early on the bullet. I don't aneal so I can't testify to that.
Re: Explain this if you can
Could be many contributing factors, but you appear to have them all, in spades. Thick neck, severe shoulder angle, no VLD chamfering and probably more than I can think of? A thorough review of the process is indicated.
Good luck, BB
Could be many contributing factors, but you appear to have them all, in spades. Thick neck, severe shoulder angle, no VLD chamfering and probably more than I can think of? A thorough review of the process is indicated.
Good luck, BB
Re: Explain this if you can
My first guess is you screwed the seating die too far down into the press, and the die made contact with the shoulder when seating and crushed the case. If so, I would unscrew your die about 6 or 7 turns, and check it on an empty case to make sure you are not making contact on the shoulder.
Next, If you are not making contact on the shoulder with the die, then you have something causing tension and not allowing the bullet to seat smoothly. An unchamfered case mounth can catch on the bottom of the bullet and stick in the neck and fold the shoulders. But my guess is the first option! Recheck your die, and let us know.
My first guess is you screwed the seating die too far down into the press, and the die made contact with the shoulder when seating and crushed the case. If so, I would unscrew your die about 6 or 7 turns, and check it on an empty case to make sure you are not making contact on the shoulder.
Next, If you are not making contact on the shoulder with the die, then you have something causing tension and not allowing the bullet to seat smoothly. An unchamfered case mounth can catch on the bottom of the bullet and stick in the neck and fold the shoulders. But my guess is the first option! Recheck your die, and let us know.
Re: Explain this if you can
Makes 3 of us. Over annealed. Doesnt matter how your dies are lined up, if you over anneal the brass is so soft it just can't take the pressure seating a bullet with tension. That pic looks familiar ... Oh yeah I did the same damn thing
Makes 3 of us. Over annealed. Doesnt matter how your dies are lined up, if you over anneal the brass is so soft it just can't take the pressure seating a bullet with tension. That pic looks familiar ... Oh yeah I did the same damn thing
Re: Explain this if you can
nice 243 "birdbath", did that once trying to push a .257 in a .243 case. I keep the different bullet size seperated better.
nice 243 "birdbath", did that once trying to push a .257 in a .243 case. I keep the different bullet size seperated better.
Re: Explain this if you can
To the OP, what did you/were you doing at the time?(more info please) We are all guessing ,but need to know what you found out.(or is this just entertainment for you
)
To the OP, what did you/were you doing at the time?(more info please) We are all guessing ,but need to know what you found out.(or is this just entertainment for you
)Similar threads